This report discusses the result of different austempering holding times and their effect on the material's hardness, ductility and yield strength. AISI 5160 steel samples were heated until they were entirely austenite and then subjected to the austempering process, submerged in a 600°F salt bath for 1, 2, 5, 30, or 90 minutes depending on the sample. Some samples were also heat-treated using water quenching and annealing for comparison. The samples were then cut, ground, and polished using standard sample preparation methods for analysis using optical microscopy, scanning electron microscopy, and x-ray diffraction. Separate samples in the form of tensile testing bars were prepared similarly. Vickers microhardness, Rockwell hardness, and tensile testing was performed.

• This report represents the work of one or more WPI undergraduate students submitted to the faculty as evidence of completion of a degree requirement. WPI routinely publishes these reports on its website without editorial or peer review.

Creator

• Al-Shawk, Abdullah Hussein
• Abdallah, Jocelyn

Publisher

• Worcester Polytechnic Institute

Identifier

• E-project-043020-065013

Advisor

• Yang, Mei
• Sisson, Richard D.

Year

• 2020

Date created

• 2020-04-30

Resource type

• Major Qualifying Project

Major

• Mechanical Engineering

Rights statement

• In Copyright